Pang-bô͘:Infobox aluminium

A-lú-mih,  ₁₃Al

A-lú-mih ê kng-phó͘ sòaⁿ (spectral lines)
Ki-pún sèng-chit
Miâ, hû-hō	a-lú-mih, Al
Phian-miâ	aluminum (US)
Gōa-hêng	kim-sio̍k-khoán phú-gîn-sek
A-lú-mih tī chiu-kî-piáu lāi ê ūi-tì
B ↑ Al ↓ Ga magnesium ← a-lú-mih → ke-sò͘
Goân-chú-hoan	13
Goân-chú-liōng (±)	26.9815385(7)
Goân-sò͘ lūi-pia̍t	āu-kòe-tō͘ kim-sio̍k ū-sî hong hun chò lūi-kim-sio̍k
Cho̍k, hun-khu	13 cho̍k, p khu
Chiu-kî	tē 3 chiu-kî
Tiān-chú pâi-lia̍t	[Ne] 3s2 3p1
per shell	2, 8, 3
Bu̍t-lí sèng-chit
Siòng	kò͘-thé
Iûⁿ-tiám	933.47 K ​(660.32 °C, ​1220.58 °F)
Hut-tiám	2743 K ​(2470 °C, ​4478 °F)
Bi̍t-tō͘  (sek-un)	2.70 g·cm−3
2.375 g·cm−3
Iûⁿ-hoà-jia̍t	10.71 kJ·mol−1
Cheng-hoat-jia̍t	284 kJ·mol−1
Jia̍t-iông-liōng	24.20 J·mol−1·K−1
cheng-khì-ap P (Pa) 1 10 100 1 k 10 k 100 k tī T (K) 1482 1632 1817 2054 2364 2790
Goân-chú sèng-chit
Sng-hòa-sò͘	3, 2, 1, −1, −2 ​(an amphoteric oxide)
Tiān-hū-tō͘	Pauling scale: 1.61
Tiān-lī-lêng	1st: 577.5 kJ·mol−1 2nd: 1816.7 kJ·mol−1 3rd: 2744.8 kJ·mol−1 (more)
Goân-chú pòaⁿ-kèng	empirical: 143 pm
Kiōng-kè pòaⁿ-kèng	121±4 pm
Van der Waals pòaⁿ-kèng	184 pm
Cha̍p-lio̍k
Chiⁿ-thé kò͘-chō	​face-centered cubic (fcc)
Siaⁿ-sok (sòe kùn-á)	(rolled) 5000 m·s−1 (at r.t.)
Jia̍t-phòng-tiòng	23.1 µm·m−1·K−1 (at 25 °C)
Jia̍t-thoân-tō-lu̍t	237 W·m−1·K−1
Tiān-chó͘-lu̍t	28.2 nΩ·m (at 20 °C)
Chû-sèng	paramagnetic
Young hē-sò͘	70 GPa
Shear hē-sò͘	26 GPa
Bulk hē-sò͘	76 GPa
Poisson pí	0.35
Mohs ngē-tō͘	2.75
Vickers ngē-tō͘	160–350 MPa
Brinell ngē-tō͘	160–550 MPa
CAS teng-kì pian-hō	7429-90-5
Le̍k-sú
Chhui-chhek	Antoine Lavoisier (1787)
Siōng chá hû-lî	Hans Christian Ørsted (1825)
hō-miâ	Humphry Davy (1807)
Chòe ún-tēng ê tông-ūi-sò͘
Chú bûn-chiong: a-lú-mih ê tông-ūi-sò͘
iso NA half-life DM DE (MeV) DP 26Al trace 7.17×105 y β 1.17 26Mg ε – 26Mg γ 1.8086 – 27Al 100% 27Al is stable with 14 neutrons